水性木器漆用乳液THYOSIL E1549
Description描述
THYOSIL E1549 is an acrylic emulsion polymer designed for manufacturing primers and topcoats for interior wood. It provides good early sandability after short drying.
是一款丙烯酸乳液聚合物，为家具或室内木器底漆和面漆所设计。提供好的打磨性和快干性能。
Characteristics特性
Recommended as a sealer. It gives excellent clarity when is applied on both dark and light woods.
具有清晰通透的质感，可以适于明或暗的木材。
The excellent selfcrosslinking chemistry is responsible for its fast curing time, good stain and block resistance. 优异的自交联化学特性，支持快速固化，抗沾污抗龟裂。
Advantages优势
ü Excellent resistance to household chemicals优异的抗家用（日用）化学腐蚀性
ü Very good adhesion非常好的附着力
ü Low water absorption 低吸水性
ü Highly sandability 高打磨性
Compatibility配伍性
THYOSIL E1549 is compatible with emulsions and resins manufactured by DIRANSA.
可以与DIRANSA 产的相关树脂和乳液相配
Typical Properties典型值
These properties are typical, do not constitute specifications
Appearance外观 | Light yellow opaque liquid淡黄色不透明液体 |
Solids (%) 固含量 | 40 |
pH | 8.0 |
Viscosity a 25ºC (cP)粘度 | < 100 |
MFFT (ºC)成膜温度 | 53 |
Particle size (nm)粒径 | 110纳米 |
Dried film干膜 | Clear without residual tack成膜干后清晰不回粘 |
Starting Formulation基础配方（底漆）
Sealer 普通木材 | Sealer for wood with high tannin content 单宁含量高的木材 | |
Raw material原料 | (%) | (%) |
THYOSIL E1549 | 40,0 | 75,0 |
Water水 | 50.9 | 8.0 |
Dowanol DPM (1)二丙二醇单甲醚 | 6.0 | 11.4 |
Butyl Glycol 丁基乙二醇 | 3.0 | 5.4 |
BYK 024 (2) 消泡剂 | 0.1 | 0.2 |
Total | 100,00 | 100,00 |
1: Dow; 2: Byk Chemie
Typical properties: 典型特性（底漆）
Test测试 | Sealer 普通木材 | Sealer for wood with high tannin content 单宁含量高的木材 |
Solid content 固含量 | 16% | 30% |
Viscosity Cup Ford N°4 at 25°C 粘度4号福特杯 | 10 sec秒 | 20 sec秒 |
pH | 7.5 | 8.0 |
Application应用
· A smooth surface is obtained by sand the wood with #150-320 grit sandpaper.
· 用# 150 - 320砂纸把木头的表面打磨光滑。
· After applying a first coating, wait until it gets dried. Then sand the applied wood using #320 grit sandpaper.
· 油完第一层后，等到它变干。然后再使用# 320砂纸打磨。
· A second coat is applied and the wood is left for two weeks driying before performing the quality tests.
· 油完第二层后，放置2周后测试其品质性能。
Test测试 | Result结果 |
Film appearance 成膜外观 | Good好 |
Gloss 亮度 | Good好 |
Adhesion 附着力 | Excellent非常好 |
Water proof 耐水性 | Excellent非常好 |
Ethanol 50% resistance 抗50%的乙醇 | Excellent非常好 |
Block resistance 抗结块 | Excellent非常好 |
Formulation Tips 配方提示
»Coalescent（成膜助剂）: THYOSIL E1549 could be used at normal temperatures with the addition of coalescing solvents. The selection of an optimum coalescing system depends on the required drying rate, temperature and relative humidity. It is usually recommended 30% of coalescing solvents but it may be used lower levels depending on the porosity of the substrate, the type of application equipment, moisture conditions and co-solvents used in the formulation. Reducing the amount of coalescent allows faster drying but an excessive reduction may result in poorer film formation and consequently the loss of the stain resistance. Various types of coalescing may be used. It must be determined for each application.
It is recommended to allow the formulations equilibrating for at least 8 hours after addition of coalescing agents to obtain consistency results in the tests performed.
THYOSIL E1549 可以在常温下可以与溶剂混合，根据所需要的干燥速度,温度和湿度，选择最佳的配比。可以在常温下可以添加成膜助剂，根据所需要的干燥速度,温度和湿度，选择最佳的配比。通常推荐使用 30%的成膜助剂（与配方中E1549的固含量相比），也可以低于或高于此水平，取决于基材的具体特性，所使用的设备，水分含量等条件。减少成膜助剂的使用干燥速度会快，但若添加太少会影响成膜性，同时还会减少防污性能。可以使用各种成膜助剂，它必须适合所需要的应用，添加的成膜助剂要8小时前后测试结果没有变化。
»Rheology Modifiers: 流变改性剂We suggest the use of associative thickeners. Keep in mind that the efficiency of urethane associative thickeners depends largely on the selection of coalescing adopted
我们推荐使用缔合型增稠剂，记住聚氨酯缔合增稠剂的效果取决于成膜助剂的选择。
»Antifoam:消泡剂Antifoam should be tested in each case. Care must be taken with the concentration chosen as an excess of antifoaming can cause fish eyes defects or loss of transparency of the film.